I’m not above taking knives, chisels, drills, and saws to prints as necessary, but this is usually reserved for functional/not often seen prints.
If I am looking to improve surface finish there really isn’t a substitute for sanding. I deal with the fuzzies with my hot air solder station. Just wave some hot air over the sanded surface and you’ll get quite a bit of shine back.
Now that I’ve (nearly) finished building a Voron I am somewhat tempted to give vapor smoothing a try.
I’ve never done it, but I also wasn’t printing with a material that even supported it until I started building my Voron. Now that I’m nearly done I am wrestling some with going back to PETG (somewhat more likely to be recycled if you put it in your recycling), PLA (could maybe be composted if it doesn’t get sorted out/will eventually break down in. A landfill), or ABS/ASA (no hopes or dreams here, but man my Voron does seem to print it well).
I have 6 kg of ASA for some functional prints. I’m sure I’ll vapor smooth some of it. Printing hassles of ABS/ASA aside, vapor smoothing seems like it offers amazing surface finishes. I really don’t know why you don’t see more of it? If you don’t need dimensional accuracy it should be a big time saver.
You are not logged in. However you can subscribe from another Fediverse account, for example Lemmy or Mastodon. To do this, paste the following into the search field of your instance: !3dprinting@lemmy.world
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at:
!functionalprint@kbin.social
or !functionalprint@fedia.io
There are CAD communities available at:
!cad@lemmy.world or !freecad@lemmy.ml
Rules
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Straight from the printer as often as possible.
I’m not above taking knives, chisels, drills, and saws to prints as necessary, but this is usually reserved for functional/not often seen prints.
If I am looking to improve surface finish there really isn’t a substitute for sanding. I deal with the fuzzies with my hot air solder station. Just wave some hot air over the sanded surface and you’ll get quite a bit of shine back.
Now that I’ve (nearly) finished building a Voron I am somewhat tempted to give vapor smoothing a try.
What do you think of an acetone vapor bath?
I’ve never done it, but I also wasn’t printing with a material that even supported it until I started building my Voron. Now that I’m nearly done I am wrestling some with going back to PETG (somewhat more likely to be recycled if you put it in your recycling), PLA (could maybe be composted if it doesn’t get sorted out/will eventually break down in. A landfill), or ABS/ASA (no hopes or dreams here, but man my Voron does seem to print it well).
I have 6 kg of ASA for some functional prints. I’m sure I’ll vapor smooth some of it. Printing hassles of ABS/ASA aside, vapor smoothing seems like it offers amazing surface finishes. I really don’t know why you don’t see more of it? If you don’t need dimensional accuracy it should be a big time saver.