I have some Fiberology PA12+CF15 blend (link) from a long time ago and recently got around to using it. I am amazed to say the least! It prints easier than PETG, even without an enclosure. Only downside is that it is much more expensive per kg, although it is lower density so I don’t seem to be going through it as quickly as other filaments.
I recently purchased some PC Blend with CF from Prusa as well. I haven’t gotten to print it yet, but I’ve heard very good things about it, too.
What less common filaments do you fine folks like using?
eSun PA-HT CF - nylon and CF in a 290C extrusion temp mix. My biggest problem is that I’ve never managed to get the support settings right so supports tend to be structurally bonded to the part and require a dremel to remove.
The other is the eSun PA-LW, which I haven’t found a good use for yet because it’s so @#$@#%$%@ oozy that it pretty much only produces a decent part when in spiral mode. Makes fantastically light parts though.
I dusted off a sealed roll of polymaker natural ASA for my CR10 V2 pro, trying to print parts for my motorcycle and cars that were previously printed in PLA+. So far a few large parts have warped about 2/3rds of the way through. I purchased a PEI magnetic bed and am now using an enclosure. The benchy i printed looks perfect tho. If i can get it dialed in, i think it will be my favorite.
You are not logged in. However you can subscribe from another Fediverse account, for example Lemmy or Mastodon. To do this, paste the following into the search field of your instance: !3dprinting@lemmy.world
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at:
!functionalprint@kbin.social
or !functionalprint@fedia.io
There are CAD communities available at:
!cad@lemmy.world or !freecad@lemmy.ml
Rules
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
Be respectful, especially when disagreeing. Everyone should feel welcome here.
No porn (NSFW prints are acceptable but must be marked NSFW)
No Ads / Spamming / Guerrilla Marketing
Do not create links to reddit
If you see an issue please flag it
No guns
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
eSun PA-HT CF - nylon and CF in a 290C extrusion temp mix. My biggest problem is that I’ve never managed to get the support settings right so supports tend to be structurally bonded to the part and require a dremel to remove.
The other is the eSun PA-LW, which I haven’t found a good use for yet because it’s so @#$@#%$%@ oozy that it pretty much only produces a decent part when in spiral mode. Makes fantastically light parts though.
What is PA-LW like as far as hardness?
I dusted off a sealed roll of polymaker natural ASA for my CR10 V2 pro, trying to print parts for my motorcycle and cars that were previously printed in PLA+. So far a few large parts have warped about 2/3rds of the way through. I purchased a PEI magnetic bed and am now using an enclosure. The benchy i printed looks perfect tho. If i can get it dialed in, i think it will be my favorite.
I love ASA for exterior fixes around the house. Durable, stable, but - as you’ve found - a bit finnicky about warping.